Refractory plastic is made of refractory aggregate and powder, raw clay and chemical compound binder and admixture. After mixing, extruding into brick shape, packaging and storage for a certain time, it still has good plasticity, and can be constructed by tamping method.
Wearing resistant plastic refractory is made from corundum, silicon carbide, special grade bauxite raw materials, ultra micro powder, composite binders, additives and plasticizer are added into raw material. It has good plasticity, long storage time, and its strength increases with the raising of temperature, which ensures good mechanical strength and abrasion resistance.
According to the type of binder can be divided into aluminum sulfate, phosphoric acid, phosphate, water glass and resin combined refractory plastics. Refractory plastic has good thermal shock resistance and is easy to be constructed. It is suitable for all kinds of heating furnace, soaking furnace, annealing furnace, hot blast furnace, etc. This series of refractory material can also be used for the furnace cover of small electric arc furnace, burner of high temperature furnace and other parts.
Refractory Plastic Introduction
Plasticizer refractory is by granular and powdery material and plasticizer such as clay binder and plasticizer cooperate, then add a small amount of water, after fully mixing formed by a kind of hard mud paste shape and maintain higher plasticity in a longer period of time is not shaped refractory.
The main components of refractory plastic are granular and powdered materials. Because this kind of unshaped refractory material is mainly used in a variety of heating furnaces that do not directly contact with the melt, clay clinker and high aluminum clinker are generally used to prepare lightweight plastics.
Refractory Plastic Physiochemical Indexes
|Al2O3 % ≥||70||75||80|
|Crushing strength MPa(110℃,24h)||60||65||70|
|Modulus of rupture MPa(110℃,24h)||10||12||14|
|Thermal shock resistance(900℃, water cooling) /times||30||30||30|
|Plasticity index %||20~40||20~40||20~40|
|Setting types||Hot setting||Hot setting||Hot setting|
Wearing Resistant Plastic Refractory Applications
RS developed plastic refractory is listed into Technique promotion program of Henan Science and Technique Department. It has the advantages of convenient for construction, quick patching, high strength and abrasion resistance, excellent thermal shock resistance, won’t cracking, good airtightness and so on. Wearing resistant plastic refractory is suitable for the construction and quick repairing of CFB boiler working lining.
Methods of Preparation
Refractory plastic coarse aggregate with high aluminum refractory clinker, refractory plastic to add 10%-15% of raw clay.As raw clay has low AI2O3 content and low fire resistance, high alumina powder is used to improve the AI2O3 content of the matrix, so that it can produce more mullite in long-term use at high temperature to improve its performance. In addition, in order to extend the time of setting and hardening of high-alumina plastics, preservatives are added.
Zhengzhou Rongsheng Kiln Refractory Co.,Ltd main products are all kinds of shaped refractories and unshaped refractories, which are widely used in building materials, metallurgy, nonferrous metals, chemical industry, electric power and other industries. The company has the high temperature tunnel kiln production line, the product sells well at home and abroad, receives the customer the widespread high praise, if has the need, invites the consultation!